Typically models: A2024, A2052, A5052, A5754, A6061, A6063, A7075, etc.

Material thickness: 0.3~20mm.

Material width: 5′ (1524mm), generally 4′, i.e. 1219mm or 1250mm, can be cut to any size less than 1524mm as required.

Material length: Can be cut to any size as required. Generally 8′, i.e. 2438mm or 2500mm.

Material Properties：
1. Lightweight, metallic white luster, easy to scratch the surface, so the surface is often pasted with PVC protective film; good durability and corrosion resistance.
2. Surface treatment: sandblasting, wire drawing, or polishing, followed by anodic oxidation and chromate oxidation.

Typically types: C1020, C1100 C2100, 2200, 2300, 2400, C2600 and above for red copper (purple copper), T2-Y purple copper plate.

Hardness: C1020P-O (O on behalf of the soft material, no hardness), C1020P-1/2H (Vickers hardness HV75 ~ 120) 1/4H HV = 60 ~ 100 H HV = 80 or more HV

Thickness: 0.3mm or more (tolerance 0/-0.08)

Length and width: 610mm*1524mm.

Features:：
1. Cooper, excellent electrical and thermal conductivity, good processability, good fusion, corrosion resistance, weather ability, metallic red luster, suitable for the electrical and chemical industry
2. Brass, ductility, processability, and plating are often used for wiring equipment, instrument panels, bullet casings, etc.

Typically types: SUS304 (18-8 stainless steel, non-magnetic), SUS301 (spring stainless steel, slightly magnetic), SUS430 (magnetic, easier to rust)

Tensile strength: above 53kgf/mm2.

Material thickness: 0.1~10.0mm.

Material width: the widest 5′ (1524mm), generally 4′, i.e. 1219mm or 1250mm, can be cut to any size less than 1524mm as required.

Length of material: Can be cut to any size as required. Generally 8′, i.e. 2438mm or 2500mm.

Specific gravity: 7.95

Features:：

1. the general tolerance of the material thickness +0, -0.08, that is, the plate thickness of 2.0mm measured may only be 1.92mm.
2. The measurement of material thickness should be used a micrometer (micrometer), do not use cursor calipers.

Typically types: SPCC, CRS, SPCD, SPCE.

Hardness: 1/2H=74～89, 1/4H=65～80, 1/8H=50～71, H=89 or more.

Tensile strength: above 28kgf/mm.

Material thickness: 0.25~3.2mm.(Material above 3.2mm must be customized)

Material width: 5′ (1524mm), generally 4′, i.e. 1219mm or 1250mm, can be cut to any size less than 1524mm as required.

Length of material: Can be cut to any size as required. Generally 8′, i.e. 2438mm or 2500mm.

Material Characteristics: Iron gray luster, the surface is easy to scratch, rust, processing should pay attention to the protection and fast turn sequence.

Features:

1. The general tolerance of the material thickness +0, -0.08, that is, the plate thickness of 2.0mm measured may be only 1.92mm.
2. In order to prevent rusting of the plate can be lightly coated with anti-rust oil on the surface of the workpiece after processing, or cover the workpiece with oil cloth.

Typically types: SPHC, HRS

Tensile strength: 41~52kgf/mm or more.

Material thickness: 1.4~6.0mm (above 6mm material code SS41)

Material width: 5′ (1524mm), generally 4′, i.e. 1219mm or 1250mm, can be cut to any size less than 1524mm as required.

Length of material: can be cut to any size as required. Generally 8′, i.e. 2438mm or 2500mm.

Specific weight: 7.85

Features:

1. Black and gray luster, the surface is not easy to scratch, but easy to rust spots, processing must pay attention to remove.
2. It is not suitable for electroplating (colorful zinc plating, white zinc plating, nickel plating, tin plating…).

Typically types: Zn100-PT, Zn200-SC, Zn275-JY (GB/T 2518-2008)

Tensile strength: 41~52kgf/mm or more.

Features:

1. White metallic luster, patterned, not easy to rust on the surface, but will produce white rust spots due to corrosion.
2. Generally do not do surface treatment
3. Can not do plating (colorful zinc plating, white zinc plating, nickel plating, tin plating)